Grade 7 Babbitt Alloy - DuraKapp™#7
DuraKapp™#7 Babbitt is a general-purpose, low-speed, Lead-based Babbitt with good tensile and compression strengths under shock, load, pounding, and vibration. Kapp Alloy’s unique Precision Microcasting™ process, combined with high-purity virgin raw materials, results in the world’s strongest, most ductile Lead-based Babbitt.
DuraKapp™#7 Babbitt meets or exceeds the specifications for ASTM #7 Babbitt —also known as Heavy Pressure, Grade 7, or QQ-T-390A No. 7 Babbitt. We back all of our products with a 100% satisfaction guarantee or your money back.
Applications
- Specifically designed for use in slower speed, heavy load and pressure settings in small or large bearings
- Especially useful in older equipment to conform to scored or imperfect shafts
- Refurbishing Grade 7 bearings in heavy load and pressure applications in low speed shafts and drives. Historically found in equipment running slowly and continuously with little lubrication or maintenance
- Older slower speed rollers, drives, motors, and engines
- Air compressors
- Hydraulic pumps
- Paired with KappaTinning™ Compound and Kapp CopperBond™ Flux
Properties
|
Specification |
|
|
ASTM B23: |
Grade 7 |
|
QQ-T-90A: |
No. 7 |
|
|
|
|
Composition |
|
|
Sn (Tin): |
9.3-10.7% |
|
Sb (Antimony): |
14.0-16.0% |
|
Pb (Lead): |
Balance |
|
|
|
|
Technical Data |
|
|
Melting Temperature Range: |
464-514°F (240-268°C) |
|
Pouring Temperature: |
640°F (338°C) |
|
Brinell Hardness (@ 68°F / 20°C): |
22.5 |
|
Tensile Strength (Chill Cast): |
10,400 psi (72 MPa) |
|
Elongation at Break: |
4% |
|
Fatigue Strength: |
NA |
|
Yield Point, Compression at Temperature: |
@ 68°F (20°C) = 3,550 psi (24.5 MPa); @ 212°F (100°C) = 1,600 psi (11 MPa) |
|
Johnson’s Apparent Elastic Limit: |
@ 68°F (20°C) = 2,500 psi (17.2 MPa); @ 212°F (100°C) = 1,350 psi (9.3 MPa) |
ASTM #7 Babbitt Product Variants
DuraKapp™#7 is available in standard forms:
Custom alloys and forms are our specialty. Call Kapp Alloy with your specific project.
Also Order
Click here for DuraKapp™#7 Technical Data Sheet