KappAloy15 - 1/16" x 10 Foot Tube$24.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.062" (1.6mm) diameter x 10 ft in tube. VIEW PRODUCT -
KappAloy15 - 1/32" x 1 lb spool$49.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.032" (0.8mm) diameter x 1 lb spool. VIEW PRODUCT -
KappAloy15 - 1/32" x 14 Foot Tube$24.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.032" (0.8mm) diameter x 14 ft in tube. VIEW PRODUCT -
KappAloy15 - 1/32" x 1/2 lb spool$34.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.032" (0.8mm) diameter x 1/2 lb spool. VIEW PRODUCT -
KappAloy15 - 1/16" x 1 lb spool$44.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.062" (1.6mm) diameter x 1 lb spool. VIEW PRODUCT -
KappAloy15 - 1/8" x 1 lb spool$44.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.125" (3.2mm) diameter x 1 lb spool. VIEW PRODUCT -
KappAloy15 - 1/16" x 1/2 lb spool$29.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.062" (1.6mm) diameter x 1/2 lb spool. VIEW PRODUCT -
KappAloy15 - 1/8" x 1/2 lb spool$29.5085Sn/15Zn for high strength hand soldering Al to Al and Cu. Slushy range (390 - 500°F / 199 - 260°C) for joint build up and adjustment. Solid -.125" (3.2mm) diameter x 1/2 lb spool. VIEW PRODUCT
KappAloy15™ is a soft Tin-Zinc solder that provides more flexibility when hand soldering Aluminum to Aluminum, Aluminum to Brass, and Aluminum to Copper. This solder gives you a slushy range of 390-500°F (199-260°C) to manipulate your parts before it solidifies completely during cooling, making it ideal for hand soldering Aluminum plates and parts. KappAloy15™ is used less often in electrical connections in order to minimize the heating of electrical/electronic parts and adjacent components.
Applications
- Hand soldering Aluminum plates and parts, allows manipulation of the parts as the solder cools
- Hand soldering structural joints
- Paired with Kapp Golden™ Flux
Properties
|
Composition |
|
|
Sn (Tin): |
85% |
|
Zn (Zinc): |
15% |
|
|
|
|
Technical Data |
|
|
Melting Range: |
390-500°F (199-260°C) |
|
Tensile Strength: |
Up to 20,000 psi (Al to Al) |
|
Elongation in 2”: |
5% |
Product Variants
KappAloy15™ is available in standard forms:
- 1/32” (0.031”) (0.8mm)
- 1/16” (0.063”) (1.6mm)
- 1/8” (0.125”) (3.2mm)
Custom alloys and forms are our specialty. Call a Kapp representative to discuss what size and diameter are right for you.
Matching Kapp Golden™ Flux
Kapp Golden™ Flux has been designed specifically for soldering Aluminum to Aluminum and Copper. It is used on Aluminum to Aluminum or Aluminum to Copper wire pigtail splices, and for Aluminum to Copper, Brass or plated terminals and hot dip coating of Aluminum cable connectors to provide a low resistance contact surface. Residue is electrically conductive and slightly corrosive. Any flux residue should be removed with warm water or alcohol and a clean rag. Golden flux will char at temperatures above 550°F. DO NOT OVERHEAT FLUX.
Click here for KappAloy15™ Technical Data Sheet
Click here for KappAloy15™ Safety Data Sheet